電工鋼硅鋼片 電工鋼板通常是以鐵芯損耗和磁感應強度作為產品磁性保證值[1] [2] 。對電工鋼板性能的要求如下：鐵芯損耗（PT）低鐵芯損耗是指鐵芯在≥50Hz交變磁場下磁化時所消耗的無效電能，簡稱鐵損，也稱交變損耗，其單位為W/kg。這種由于磁通變化受到各種阻礙而消耗的無效電能，通過鐵芯發熱既損失掉電能，又引起電機和變壓器的溫升。電工鋼的鐵損（PT）包括磁滯損耗、內蒙古鄂爾多斯本地渦流損耗（Pe）和反常損耗（Pa）三部分。電工鋼板鐵損低，既可節省大量電能，又可延長電機和變壓器工作運轉時間，并簡化冷卻裝置。由于電工鋼板的鐵損所造成的電量損失占各國全年發電量的2.5％~4.5％，因此各國生產電工鋼板總是千方百計設法降低鐵損，并以鐵損作為考核產品磁性的重要指標，按產品的鐵損值作為劃分產品牌號的依據。冷軋取向電工鋼：冷軋取向電工鋼是電工鋼中的高端產品，與冷軋無取向電工鋼相比，磁性具有強烈的方向性；在易磁化的軋制方向上具有優越的高磁導率與低損耗特性。取向鋼帶在軋制方向的鐵損僅為橫向的1/3，磁導率之比為6：1。用途：冷軋取向硅鋼帶主要的用途是用于變壓器制造。

電工鋼硅鋼片In addition to the types listed above, there are also some special purpose electrical steel plates, such as 0.15 and 0.20mm thick 3％ Si cold-rolled non oriented silicon steel strips and 0.025, 0.05, and 0.1mm thick 3％ Si cold-rolled oriented silicon steel strips, used for medium and high-frequency motors, transformers, and pulse transformers； 0.7mm thick 3％ Si high-strength cold-rolled non oriented silicon steel plate for relays and power switches； High strength cold-rolled electrical steel plate for new high-speed motor rotors； Low carbon electrical steel hot-rolled thick and cold-rolled plates for magnetic shielding and high-energy accelerator electromagnets such as medical magnetic resonance tomography scanners； 4.5％ to 6.5％ Si high silicon steel plates for high-frequency motors, transformers, and magnetic shielding.Generally, motors, transformers, and other electrical components are required to have high efficiency, low power consumption, small size, and light weight. Electrical steel plates are usually guaranteed to have magnetic properties based on core loss and magnetic induction strength [1] [2]. The requirements for the performance of electrical steel plates are as follows:Low core loss (PT)Iron core loss refers to the ineffective electrical energy consumed by an iron core when magnetized in an alternating magnetic field of ≥ 50Hz, abbreviated as iron loss, also known as alternating loss, and its unit is W/kg. The ineffective electrical energy consumed due to various obstacles caused by magnetic flux changes not only loses electrical energy through the heating of the iron core, but also causes temperature rise of the motor and transformer. The iron loss (PT) of electrical steel includes three parts: hysteresis loss, eddy current loss (Pe), and anomalous loss (Pa). Electrical steel plates have low iron loss, which can save a lot of electricity, prolong the operating time of motors and transformers, and simplify cooling devices. Due to the iron loss of electrical steel plates, which accounts for 2.5％ to 4.5％ of the annual electricity generation in various countries, countries always try their best to reduce iron loss in the production of electrical steel plates, and use iron loss as the most important indicator to assess the magnetic properties of products. The iron loss value of products is used as the basis for classifying product grades. Cold rolled oriented electrical steel: Cold rolled oriented electrical steel is a high-end product in the field of electrical steel. Compared with cold rolled non oriented electrical steel, its magnetism has strong directionality； It has superior high magnetic permeability and low loss characteristics in the direction of easy magnetization rolling. The iron loss of oriented steel strip in the rolling direction is only 1/3 of that in the transverse direction, and the ratio of magnetic permeability is 6:1. Application: The main purpose of cold-rolled oriented silicon steel strip is for transformer manufacturing.Full process cold rolled non oriented silicon steel coating: The surface of the full process cold rolled silicon steel is coated with a semi transparent insulation coating, which has different codes in different standards. Taking Baosteel‘s Q/BQB 480 2014 as an example: